FD-H001 Matt Finish Zinc Rich Epoxy Paint - 20kg for Heavy Use

FD-H001 two-component epoxy anti-corrosion coating for steel substrates. Supplied in liquid form.

Reference price (FOB)

US $2.5-6.5 / kg

Quantity	Reference price
100-999 kg	USD 6.50 / kg
1,000-999,999 kg	USD 4.50 / kg
1,000,000+ kg	USD 2.50 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings

Product specifications

Model NO.: FD-H001
Color: Grey
Appearance: Liquid
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Trademark: Singal
Transport Package: Barrel Package in Pallet
Specification: 35*30
Origin: Dongying China
HS Code: 3208100000
Customization: Available
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Zinc Rich Epoxy Primer Sewage Plant Metal Protection Anti-Corrosive Paint

1. Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxy resinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Experience unparalleled protection with its highshielding property, providing superioranti-rustproperty, outstanding adhesion,and excellent oilandwaterresistance, ensuring longevity and durability.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2. Surface treatment:
The steel surface must be meticulously prepared, either shot blasted or sand blasted to Sa2.5 level, or manually rust-removed to St3 level, setting a pristine base for application.

3. Construction conditions:
Optimal application requires that the substrate temperature is at least 3°C above the dew point, with humidity below 85%, and wind force not exceeding level 3. If the temperature is below 5°C, the epoxy resin and curing agent cease reaction, halting construction. Avoid inclement weather conditions such as rain, fog, wind, and sand, as well as morning and evening condensation during outdoor applications.

4. Notes:
1. Prior to use, mechanically stir component A thoroughly, then blend it uniformly with component B.
2. To maintain the perfect consistency, regularly stir the mixture during the coating process. This prevents sedimentation, ensuring the powder-to-liquid ratio remains balanced and the paint film's quality is preserved.
3. Aim for a dry film thickness of ≥70μm, completing 1 to 2 coats for optimal results.
4. Once mixed, utilize the two-component paint within 5 hours to maintain coating excellence; exceeding this timeframe could compromise quality.
5. After using the curing agent, cover it tightly to prevent exposure to air moisture, preserving its efficacy and preventing unnecessary losses.