FD-H001 Zinc Rich Epoxy Paint for Durable Finishes

FD-H001 two-component epoxy anti-corrosion coating for steel substrates. Supplied in liquid form.

Reference price (FOB)

US $2.5-6.5 / kg

Quantity	Reference price
100-999 kg	USD 6.50 / kg
1,000-999,999 kg	USD 4.50 / kg
1,000,000+ kg	USD 2.50 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings

Product specifications

Model NO.: FD-H001
Color: Grey
Appearance: Liquid
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Trademark: Singal
Transport Package: Barrel Package in Pallet
Specification: 35*30
Origin: Dongying China
HS Code: 3208100000
Customization: Available
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Zinc Rich Epoxy Primer Sewage Plant Metal Protection Anti Corrosive Paint

1. Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxy resinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Boasting high shielding properties, this primer offers superiorprotection against rust, with exceptional adhesion, andexcellent resistance toboth oiland water.It providesa resilientfinish.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2. Surface treatment:
For optimal results, the steel surface should undergo shot blasting or sandblasting to Sa2.5 level, or manually have rust removed to St3 level.

3. Construction conditions:
Ensure the substrate temperature is at least 3°C above the dew point, and maintain a relative humidity of <85%, with wind force not exceeding level 3. When the substrate temperature drops below 5°C, halt construction as the epoxy resin and curing agent will not react. Avoid working on rainy, foggy, windy, and sandy days, as well as during morning and evening condensation periods.

4. Notes:
1. Prior to application, mechanically stir component A thoroughly, then mix evenly with component B.
2. Stir periodically throughout the coating process to prevent sedimentation, which can disrupt the powder-to-liquid ratio and impair the quality of the paint film.
3. A dry film thickness of ≥70μm is recommended, with the completion of 1 to 2 coats.
4. Use the mixed two-component paint within 5 hours to maintain coating quality.
5. Once the curing agent has been opened, seal it tightly and use promptly to avoid losses from reactions with atmospheric moisture.