WB Thermal-Resistant Acrylic Paint for High-Temperature Applications — Outdoor Water-based Intumescent Fireproof Coating

Product specifications

Model NO.

WB

Fire Prevention Mechanism

Expansion Steel Structure

Thickness

Thin

Use

Cable Fire Retardant Coating, Finish Type, Fireproof Coatings For Steel Structures, Prestressed Concrete Floor Fire Retardant Coating

Shelf Time

12 Monthes

Temperature

5-38℃

Relative Humidity

85%

Fire Resistance

2 Hours

Consumption

4.5kg/M2

Coating Thickness

2.8mm

Component

1 Component

Application

Steel Structure

Construction

Spray, Brush, Roller

Topcoat

Specialized Topcoat

Substrate

Steel

Brand

Signal

Package

20kg Barrel

Base

Acrylic

Transport Package

Barrel

Specification

35*30

Trademark

signal

Origin

China, Shandong

HS Code

3208100000

Production Capacity

50000ton/Year

Package Size

30.00cm * 30.00cm * 35.00cm

Package Gross Weight

20.000kg

Number of components

Single-component

Density

1.2kg/L

Volumetric solid content

60%

VOC

13g/L

Recommended dry film thickness

400-800μm

Theoretical coating rate

0.75m²/L

Touch dry

6 hours

Coating interval

24 hours

Shelf life

12 months

Packaging & shipping

Transport Package

Barrel

Specification

35*30

Package Size

30.00cm * 30.00cm * 35.00cm

Package Gross Weight

20.000kg

Product description

Product Name: WB Water Based Fireproof Intumescent Coating

 

Harnessing the pinnacle of American technology and embodying excellence within a state-of-the-art, fully enclosed automatic production facility, this groundbreaking product is powered by a sophisticated acrylic resin and N-P expansion flame retardant system. Revel in unmatched fire resistance that surpasses expectations, paired with superb bonding strength and a stunning decorative finish. Its user-friendly application makes it the preferred choice among professionals.

A versatile powerhouse, this coating is essential for a myriad of applications. From protecting outdoor load-bearing steel components in expansive steel structure workshops to strengthening intricate building grids, it is indispensable in the world of contemporary architecture.

Number of components	Single-component
Density	1.2kg/L
Volumetric solid content	60%
VOC	13g/L
Recommended dry film thickness	400-800μm
Theoretical coating rate	0.75m²/L
Touch dry	6 hours
Coating interval	24 hours
Shelf life	12 months