FD-H001 Anti-Rust Zinc Epoxy Primer Coating

FD-H001 two-component epoxy primer for steel substrates. Supplied in liquid form.

Reference price (FOB)

US $4-10 / kg

Quantity	Reference price
100-9,999 kg	USD 10.00 / kg
10,000-999,999 kg	USD 8.00 / kg
1,000,000+ kg	USD 4.00 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings Primers

Product specifications

Model NO.: FD-H001
Color: Grey
Appearance: Liquid
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Trademark: signal
Transport Package: Barrel Package in Pallet
Specification: 35*30
Origin: Dongying China
HS Code: 3208100000
Customization: Available
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Hot Sales High-Performance Anti-Rust Zinc Epoxy Primer for Steel Buildings

FD-H001 Anti-Rust Zinc Epoxy Primer Coating
1.Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxy resinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Highshielding property, superioranti-rustproperty, strongadhesion, and good oilandwaterresistance.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2.Surface treatment:
The steel surface is meticulously shot blasted or sand blasted to a pristine Sa2.5 level, or carefully manually rust-removed to a refined St3 level.

3.Construction conditions:
Ensure the substrate temperature is consistently 3°C higher than the dew point, with relative humidity maintained below 85%, and wind force not exceeding level 3. Construction should be halted when substrate temperatures fall below 5°C, as the epoxy resin and curing agent will cease to react. Avoid construction during adverse weather conditions such as rain, fog, strong winds, and sandy days, as well as during condensation risks in the morning and evening for outdoor projects.

4.Notes:
1. Prior to application, thoroughly utilize mechanical stirring to mix component A until uniform, followed by an even mixture with component B.
2. Consistently stir during the coating process to avert sedimentation, which could disrupt the powder to liquid balance and compromise the integrity of the paint film.
3. It is advised that the dry film thickness be maintained at ≥70μm, completing 1 to 2 robust coats.
4. Post-mixing, the two-component paint should ideally be consumed within a 5-hour timeframe. Extending beyond this period could potentially impact the coating quality.
5. Once the curing agent is depleted, ensure it is sealed tightly and used promptly to avoid losses from reactions with atmospheric water vapor.