FD-H001 20kg Dual Component Epoxy Coating - High Pressure Air Spray, Matt

FD-H001 two-component epoxy anti-corrosion coating for steel substrates.

Reference price (FOB)

US $2-10 / kg

Quantity	Reference price
100-999 kg	USD 10.00 / kg
1,000-999,999 kg	USD 6.00 / kg
1,000,000+ kg	USD 2.00 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings

Product specifications

Model NO.: FD-H001
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Transport Package: Barrel Package in Pallet
Specification: 35*30
Trademark: signal
Origin: Dongying China
HS Code: 3208100000
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Color: Grey
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Factory Price Double Component Epoxy Anti-Corrosive Primer Coating

1. Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxy resinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Highshielding property, superioranti-rustproperty, strongadhesion, and excellent oilandwaterresistance.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2. Surface treatment:
The steel surface is meticulously prepared by shot blasting or sand blasting to a pristine Sa2.5 level, or through diligent manual rust removal to achieve St3 level.

3. Construction conditions:
The substrate temperature must exceed the dew point by 3°C, with relative humidity below 85%, and wind force not exceeding level 3. When the substrate temperature drops below 5°C, the epoxy resin and curing agent cease reaction, necessitating a halt in construction activities. Avoid rainy, foggy, windy, and sandy days, as well as morning and evening condensation for outdoor projects.

4. Notes:
1. Prior to application, ensure thorough mechanical stirring of component A for uniformity, followed by even mixing with component B.
2. Maintain regular stirring during the coating process to prevent sedimentation, which can disrupt the powder-to-liquid ratio, thus impacting the quality of the paint film.
3. It is advisable for the dry film thickness to be at least 70μm, with 1 to 2 coats applied for optimal coverage.
4. Once mixed, the two-component paint should be used within a 5-hour window to maintain coating integrity.
5. After depletion of the curing agent, ensure the container is sealed tightly and used promptly to avert losses from reactions with ambient moisture.