FD-H001 Factory Price Two-Component Epoxy Anti-Corrosive Primer Coating

FD-H001 two-component epoxy primer for steel substrates.

Reference price (FOB)

US $2-10 / kg

Quantity	Reference price
100-999 kg	USD 10.00 / kg
1,000-999,999 kg	USD 6.00 / kg
1,000,000+ kg	USD 2.00 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings Primers

Product specifications

Model NO.: FD-H001
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Transport Package: Barrel Package in Pallet
Specification: 35*30
Trademark: signal
Origin: Dongying China
HS Code: 3208100000
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Color: Grey
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Factory Price Double Component Epoxy Anti-Corrosive Primer Coating

1. Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxy resinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Boasting highshielding qualities, this coating offers superioranti-rustperformance, strongadhesion, and excellent resistance to both oilandwater.resistance.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2. Surface Treatment:
The steel surface should be meticulously shot or sand blasted to Sa2.5 level, or manually cleansed to St3 level for optimal results.

3. Construction Conditions:
Ensure the substrate temperature is at least 3°C above the dew point, with relative humidity maintained below 85%, and wind force kept at or below level 3. Construction should cease if the substrate temperature drops below 5°C, as the epoxy resin and curing agent will halt their reaction. Avoid rainy, foggy, windy, and sandy days, as well as condensation during morning and evening hours for outdoor applications.

4. Notes:
1. Prior to application, rigorously mix component A using mechanical stirring, ensuring it blends evenly with component B.
2. Stir regularly during the coating process to thwart sedimentation, which can disrupt the powder-to-liquid ratio and adversely impact the paint film's quality.
3. It is recommended that the dry film thickness be maintained at ≥70μm, with 1 to 2 coats applied for optimal protection.
4. Once mixed, the two-component paint should ideally be consumed within 5 hours to maintain coating efficacy, as exceeding this timeframe may compromise quality.
5. Once the curing agent is depleted, seal the container tightly and use promptly to prevent reactions with atmospheric moisture that could lead to material losses.