FD-H001 20kg Barrel of Dual Component Epoxy Coating - Matt Finish for Spray

FD-H001 two-component epoxy anti-corrosion coating for steel substrates. Supplied in liquid form.

Reference price (FOB)

US $2-10 / kg

Quantity	Reference price
100-999 kg	USD 10.00 / kg
1,000-999,999 kg	USD 6.00 / kg
1,000,000+ kg	USD 2.00 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings

Product specifications

Model NO.: FD-H001
Color: Grey
Appearance: Liquid
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Trademark: signal
Transport Package: Barrel Package in Pallet
Specification: 35*30
Origin: Dongying China
HS Code: 3208100000
Customization: Available
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Factory Price Dual Component Epoxy Anti-Corrosive Primer Coating

1. Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxy resinasthebasematerial, phosphateironpowder,rust-proofpigment,etc., and cured by polyamide.It is expertly engineered andpacked as dual componentsAand B.Characteristics:Boasting highshielding capacity, this coating offers superioranti-rustfeatures, strongadhesion, and excellent oilandwaterresistance.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2. Surface treatment:
The steel surface should be prepared by shot blasting or sand blasting to achieve an Sa2.5 level, or manually rust-removed to an St3 level for optimal results.

3. Construction conditions:
Ensure the substrate temperature is at least 3°C above the dew point, with relative humidity below 85% and wind force not exceeding level 3. If the substrate temperature falls below 5°C, the epoxy resin and curing agent will cease to react, and construction should be halted. Avoid undertaking work on rainy, foggy, windy, or sandy days, and during times of morning and evening condensation for outdoor projects.

4. Notes:
1. Prior to application, thoroughly mix component A using mechanical stirring, then combine it evenly with component B to ensure the highest quality.
2. Regular stirring during the application process is crucial to prevent sedimentation, which can disrupt the powder-to-liquid balance and compromise the paint film quality.
3. It is advised that the dry film thickness be at least 70μm, achieved through 1 to 2 coats.
4. After mixing, the two-component paint should ideally be used within 5 hours; exceeding this timeframe may negatively impact coating quality.
5. Once the curing agent is depleted, reseal it tightly and utilize it swiftly to prevent losses from reactions with ambient water vapor.