FD-H001 Dual Component Matt Epoxy Coating - 20kg for Air Spray and Brush

FD-H001 two-component epoxy anti-corrosion coating for steel substrates.

Reference price (FOB)

US $2-10 / kg

Quantity	Reference price
100-999 kg	USD 10.00 / kg
1,000-999,999 kg	USD 6.00 / kg
1,000,000+ kg	USD 2.00 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings

Product specifications

Model NO.: FD-H001
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Transport Package: Barrel Package in Pallet
Specification: 35*30
Trademark: signal
Origin: Dongying China
HS Code: 3208100000
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Color: Grey
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Factory Price Dual Component Epoxy Anti-Corrosive Primer Coating

1.Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxy resinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispackaged in dual componentsAand B.Characteristics:Highshielding property, superioranti-rustproperty, strongadhesion, and excellent oilandwaterresistance.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2.Surface treatment:
The steel surface is treated by shot blasting or sand blasting to Sa2.5 level, or manually rust-removed to St3 level.

3.Construction conditions:
The substrate temperature should be 3°C above the dew point, with relative humidity below 85%, and wind force not exceeding level 3. If the substrate temperature drops below 5°C, halt construction as the epoxy resin and curing agent cease reacting. Avoid adverse weather conditions such as rain, fog, strong winds, or condensation, especially during outdoor applications.

4.Notes:
1. Prior to application, thoroughly mix component A using mechanical stirring, and then blend evenly with component B.
2. Stir regularly during the coating process to prevent sedimentation and ensure a balanced powder-to-liquid ratio, maintaining optimal paint film quality.
3. The dry film thickness should be ≥70μm with 1 to 2 coats recommended for best results.
4. Utilize the mixed two-component paint within 5 hours to ensure coating integrity. Extended time may compromise quality.
5. Seal the curing agent tightly after use and consume promptly to avoid losses due to reactions with ambient water vapor.