FD-H001 Epoxy Zinc Rich Primer Paint for All Construction Methods

FD-H001 two-component epoxy primer for steel substrates.

Reference price (FOB)

US $4-10 / kg

Quantity	Reference price
100-9,999 kg	USD 10.00 / kg
10,000-999,999 kg	USD 8.00 / kg
1,000,000+ kg	USD 4.00 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings Primers

Product specifications

Model NO.: FD-H001
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Transport Package: Barrel Package in Pallet
Specification: 35*30
Trademark: signal
Origin: Dongying China
HS Code: 3208100000
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Color: Grey
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Steel Structure Anti-Corrosion Epoxy Zinc Rich Primer Paint

1.Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxyresinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Highshielding property, superioranti-rustproperty, strongadhesion, and good oilandwaterresistance.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2.Surface treatment:
The steel surface is skillfully shot blasted or meticulously sand blasted to meet the demanding Sa2.5 level, or meticulously rust-removed to achieve St3 level.

3.Construction conditions:
The substrate temperature must always be maintained at 3°C higher than the dew point, with relative humidity kept below 85% and wind force contained at or below level 3. For optimal results, cease construction when the substrate temperature falls below 5°C, as the epoxy resin and curing agent cease to react. Avoid construction during inclement weather such as rain, fog, or high winds, and during periods of condensation in the early morning and evening for outdoor applications.

4.Notes:
1. Prior to application, mechanically stir component A to a uniform consistency before seamlessly blending it with component B.
2. Maintain regular stirring throughout the coating process to prevent sedimentation, which could disrupt the powder-to-liquid balance and compromise the paint film quality.
3. For optimal protection, ensure the dry film thickness is at least 70μm, recommending 1 to 2 coats for ultimate coverage.
4. Utilize the mixed two-component paint within a 5-hour window to maintain top-notch coating quality.
5. After using the curing agent, seal it tightly and use it promptly to avert losses from reactions with airborne water vapor.