Two-Component Epoxy Zinc-Rich Primer

Name: Two-Component Epoxy Zinc-Rich Primer
Brand: SINGAL PAINT

Two-component epoxy primer for steel substrates.

Reference price (FOB)

US $3.5-4 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings Primers

Performance

Main Raw Material: Epoxy
Level: Primer
Components: Film-forming material
Film-forming mechanism: Conversion Type
Luster: Matt
Coating Thickness: Wet Film:80um Dry Film: 40um
Number of components: Two-component
Color: Grey
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24 h, Fully cured 7 days
Coating thickness: Wet film:80um Dry film: 40um

Application

Method: Spray
Drying Method: Air Drying
Substrate: Steel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Roller
Mixing ratio: 10:1
Construction method: High pressure airless spray, air spray, Brush, Roller

Packaging

Weight: 20 kg/Barrel
Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000 kg
Shelf life: 12 months

Product description

Product Description

Product Name: Anti-Rust Epoxy Zinc Primer Anti Corrosion Coating for Industrial Steel Protection

1. Introduction:

Epoxy zinc_-rich primer is a two_-component coating with epoxy resin as the base material, phosphor iron powder, rust-proof pigment, etc., and cured by polyamide. It ispacked by dual components A and B. Characteristics: High shielding property, superior anti-rust property, strong adhesion, and good oil and water resistance.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24 h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction method	High pressure airless spray, air spray, Brush, Roller
Shelf life	12 months

2. Surface treatment:
The steel surface is shot blasted or sand blasted to Sa2.5 level, or manually rust-removed to St3 level.

3. Construction conditions:
The substrate temperature must be 3°C higher than the dew point, relative humidity <85%, wind force ≤ level 3; when the substrate temperature is lower than 5°C, the epoxy resin and curing agent stop reacting and construction should be stopped. Avoid rainy, foggy, windy and sandy days and condensation in the morning and evening for outdoor construction.

4. Notes:
1. Before use, use mechanical stirring to mix component A evenly, and then mix it evenly with component B.
2. Regularly stir during the coating process to prevent sedimentation, which can cause an imbalance in the powder to liquid ratio and affect the quality of the paint film.
3. It is recommended that the dry film thickness be ≥70μm, and 1 to 2 coats be completed.
4. After mixing, the two-component paint is generally used up within 5 hours. Exceeding the time may affect the coating quality.
5. After the curing agent is used up, it must be covered tightly and used up as soon as possible to prevent losses caused by reactions with water vapor in the air.