FD-H001 All-Weather Matt Epoxy Primer Coating - 20kg for Outdoor Durability

Name: FD-H001 All-Weather Matt Epoxy Primer Coating - 20kg for Outdoor Durability
SKU: MIC-ERPYJkcTuFVA

FD-H001 two-component epoxy primer for steel substrates. Intended for outdoor use.

Reference price (FOB)

US $4-10 / kg

Quantity	Reference price
100-9,999 kg	USD 10.00 / kg
10,000-999,999 kg	USD 8.00 / kg
1,000,000+ kg	USD 4.00 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings Primers

Product specifications

Model NO.: FD-H001
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Transport Package: Barrel Package in Pallet
Specification: 35*30
Trademark: signal
Origin: Dongying China
HS Code: 3208100000
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Color: Grey
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Hot Sales High-Performance Anti Rust Zinc Epoxy Primer for Steel Buildings

FD-H001 All-Weather Matt Epoxy Primer Coating - 20kg for Outdoor Durability
1. Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxy resinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Highshielding property, superioranti-rustproperty, strongadhesion, and excellent oilandwaterresistance.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2. Surface treatment:
The steel surface undergoes shot blasting or sand blasting to Sa2.5 level, or manual rust-removal to reach St3 level.

3. Construction conditions:
For optimal application, ensure the substrate temperature is at least 3°C above the dew point, with relative humidity below 85%, and wind force not exceeding level 3. If the substrate temperature drops below 5°C, the epoxy resin and curing agent halt reactions, requiring a pause in construction. Avoid outdoor application during rainy, foggy, windy, or sandy weather, and steer clear of morning and evening condensation.

4. Notes:
1. Prior to use, mechanically stir component A thoroughly, then blend evenly with component B.
2. Continuously stir during the application process to prevent sedimentation, which can disrupt the powder-liquid balance and compromise the paint film's quality.
3. Aim for a dry film thickness of at least 70μm, applying 1 to 2 coats.
4. After mixing, it is crucial to use the two-component paint within 5 hours. Exceeding this timeframe may degrade the coating quality.
5. Once the curing agent is depleted, seal it tightly and utilize it promptly to prevent any losses from reactions with water vapor in the atmosphere.