FD-H001 Dual Component Epoxy Coating - 20kg, Perfect for High Pressure Spray

Name: FD-H001 Dual Component Epoxy Coating - 20kg, Perfect for High Pressure Spray
SKU: MIC-BaMrftcUvbRl

FD-H001 two-component epoxy anti-corrosion coating for steel substrates.

Reference price (FOB)

US $2-10 / kg

Quantity	Reference price
100-999 kg	USD 10.00 / kg
1,000-999,999 kg	USD 6.00 / kg
1,000,000+ kg	USD 2.00 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings

Product specifications

Model NO.: FD-H001
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Transport Package: Barrel Package in Pallet
Specification: 35*30
Trademark: signal
Origin: Dongying China
HS Code: 3208100000
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Color: Grey
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Factory Price Double Component Epoxy Anti-Corrosive Primer Coating

1. Introduction:

Our epoxy coatingenriched with zinc,_-is a richprimer thatisatwo_-componentcoating.Formulated withepoxy resinasthebasematerial, this coating incorporates phosphor ironpowder, offeringrust-proofpigment,and is cured by the power ofpolyamide. This remarkable productispacked conveniently by dual components,Aand B.Characteristics:Boasting highshielding capabilities, this coating provides superior anti-rust properties,strong adhesion, and excellent resistance to oiland water.Its durabilityandversatility make it an ideal choice forvaried environments.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2. Surface treatment:
Achieve optimal performance by shot blasting or sand blasting the steel surface to Sa2.5 level, or removing rust manually to St3 level.

3. Construction conditions:
Ensure the substrate temperature exceeds the dew point by 3°C, with relative humidity below 85% and wind force at or below level 3. Avoid application when the substrate temperature falls under 5°C, as reaction halts between the epoxy resin and curing agent. Refrain from construction on rainy, foggy, windy days, or during morning and evening condensation outdoors.

4. Notes:
1. Prior to application, employ mechanical stirring to thoroughly mix component A before combining evenly with component B.
2. Stir regularly during application to prevent sedimentation, which can skew the powder-to-liquid ratio and compromise the paint film's quality.
3. Aim for a dry film thickness of ≥70μm, completing 1 to 2 coats for optimal results.
4. Use the mixed two-component paint within 5 hours to maintain coating quality. Prolonged storage may degrade the product.
5. Seal the curing agent tightly after use and consume promptly to prevent reaction with atmospheric moisture, which could lead to product loss.