FD-H001 Dual Component Epoxy Coating High Pressure Air Spray

Name: FD-H001 Dual Component Epoxy Coating High Pressure Air Spray
SKU: MIC-UfYRQqWSsMpc

FD-H001 two-component epoxy anti-corrosion coating for steel substrates.

Reference price (FOB)

US $2-10 / kg

Quantity	Reference price
100-999 kg	USD 10.00 / kg
1,000-999,999 kg	USD 6.00 / kg
1,000,000+ kg	USD 2.00 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings

Product specifications

Model NO.: FD-H001
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Transport Package: Barrel Package in Pallet
Specification: 35*30
Trademark: signal
Origin: Dongying China
HS Code: 3208100000
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Color: Grey
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Factory Price Dual Component Epoxy Anti-Corrosive Primer Coating

1. Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxy resinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Highshielding property, superioranti-rustproperty, strongadhesion, and good oilandwaterresistance.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2. Surface treatment:
The steel surface is meticulously shot blasted or sand blasted to Sa2.5 level or manually rust-removed to St3 level, ensuring a pristine preparation for coating.

3. Construction conditions:
To ensure optimal application results, maintain the substrate temperature at least 3°C above the dew point, with relative humidity under 85%, and wind force not exceeding level 3. If the substrate temperature falls below 5°C, the epoxy resin and curing agent cease to react, necessitating a halt in construction. Avoid proceeding on rainy, foggy, windy, or sandy days, and be cautious of morning and evening condensation during outdoor projects.

4. Notes:
1. Prior to usage, engage in thorough mechanical stirring to achieve a uniform mix of component A before combining it evenly with component B.
2. Consistently stir throughout the coating process to avert sedimentation, which can unbalance the powder to liquid ratio, impacting the paint film's quality.
3. It is advised to achieve a dry film thickness of ≥70μm, completing 1 to 2 coats for optimal coverage.
4. Once mixed, the two-component paint should be used within 5 hours to preserve coating quality.
5. After utilizing the curing agent, securely cover it and use it promptly to prevent adverse reactions with airborne water vapor, thus avoiding potential losses.