FD-H001 Efficient Matt Epoxy Paint Primer for High Pressure Airless Use

Product Description

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxyresinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Highshielding property, offering superioranti-rustproperty. It boasts strongadhesion, and excellent oilandwaterresistance.

2. Surface treatment:
The steel surface is expertly prepared by shot blasting or sandblasting to Sa2.5 level, or manually rust-removed to St3 level for optimal results.

3. Construction conditions:
The substrate temperature must be at least 3°C above the dew point, with relative humidity under 85%, and wind force no greater than level 3. If the substrate temperature falls below 5°C, the epoxy resin and curing agent reaction halts, necessitating a pause in construction. Avoid outdoor construction during rainy, foggy, windy, or sandy conditions, as well as during morning and evening condensation.

4. Notes:
1. Prior to use, thoroughly mix component A using mechanical stirring, then combine evenly with component B.
2. Regular stirring during application is essential to prevent sedimentation, which could lead to an imbalanced powder-to-liquid ratio and compromise the paint film's quality.
3. It is recommended to achieve a dry film thickness of at least 70μm, with the application of 1 to 2 coats.
4. Once mixed, the two-component paint should generally be used within 5 hours to maintain coating quality.
5. After using the curing agent, seal it tightly and use it promptly to prevent losses due to reactions with atmospheric water vapor.