FD-H001 Epoxy Zinc Rich Primer Paint for Brush, Roller, and Spray Applications

Product Description

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxyresinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Highshielding property, superioranti-rustproperty, strongadhesion, and good oilandwaterresistance.

2.Surface treatment:
The steel surface is shot blasted or sand blasted to Sa2.5 level, or manually rust-removed to St3 level.

3.Construction conditions:
To ensure optimal application, the substrate temperature should consistently remain 3°C above the dew point, with a relative humidity of less than 85%, and wind force not exceeding level 3. Construction must cease if temperatures fall below 5°C, as the epoxy resin and curing agent cease to react. Avoid construction in rainy, foggy, windy, and sandy conditions, as well as during morning and evening condensation periods.

4.Notes:
1. Prior to use, ensure mechanical stirring thoroughly mixes component A; then, mix evenly with component B for a perfect blend.
2. Maintain regular stirring throughout the coating process to prevent sedimentation, which could disrupt the powder-to-liquid balance and compromise paint film quality.
3. For best results, the dry film thickness should be ≥70μm, achieved in 1 to 2 coats.
4. Once mixed, utilize the two-component paint within 5 hours to preserve coating quality. Beyond this, the effectiveness may diminish.
5. After using the curing agent, promptly and tightly seal it to prevent degradation from atmospheric moisture, ensuring it is used as swiftly as possible.