FD-H001 Epoxy Zinc Rich Primer Paint for High Pressure and Air Spray Methods

Name: FD-H001 Epoxy Zinc Rich Primer Paint for High Pressure and Air Spray Methods
SKU: MIC-qfgrLJNETbYQ

FD-H001 two-component epoxy primer for steel substrates.

Reference price (FOB)

US $4-10 / kg

Quantity	Reference price
100-9,999 kg	USD 10.00 / kg
10,000-999,999 kg	USD 8.00 / kg
1,000,000+ kg	USD 4.00 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings Primers

Product specifications

Model NO.: FD-H001
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Transport Package: Barrel Package in Pallet
Specification: 35*30
Trademark: signal
Origin: Dongying China
HS Code: 3208100000
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Color: Grey
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Steel Structure Anti-Corrosion Epoxy Zinc Rich Primer Paint

1.Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxyresinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Highshielding property, superioranti-rustproperty, strongadhesion, and good oilandwaterresistance.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2.Surface treatment:
The steel surface is shot blasted or sand blasted to Sa2.5 level, or manually rust-removed to St3 level.

3.Construction conditions:
The substrate temperature must be at least 3°C above the dew point, with relative humidity under 85%, and wind forces not exceeding level 3. When substrate temperatures fall below 5°C, the epoxy resin and curing agent cease to react, halting construction. Avoid weather conditions like rain, fog, wind, sandy environments, and condensation during mornings and evenings for outdoor work.

4.Notes:
1. Prior to use, ensure thorough mechanical stirring of component A before evenly mixing with component B.
2. Maintain regular stirring throughout the coating process to prevent sedimentation, which can disrupt the powder-to-liquid balance and compromise the paint film quality.
3. Recommended dry film thickness should be no less than 70μm, with the application of 1 to 2 coats.
4. Once mixed, the two-component paint should be utilized within 5 hours to maintain optimal coating quality.
5. Seal the curing agent tightly after use and consume swiftly to avert losses from air moisture reactions.