FD-H001 Epoxy Zinc Rich Primer Paint: Perfect for High Pressure Airless Spray

Name: FD-H001 Epoxy Zinc Rich Primer Paint: Perfect for High Pressure Airless Spray
SKU: MIC-ifNRzALMObpu

FD-H001 two-component epoxy primer for steel substrates. Supplied in liquid form.

Reference price (FOB)

US $4-10 / kg

Quantity	Reference price
100-9,999 kg	USD 10.00 / kg
10,000-999,999 kg	USD 8.00 / kg
1,000,000+ kg	USD 4.00 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings Primers

Product specifications

Model NO.: FD-H001
Color: Grey
Appearance: Liquid
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Trademark: signal
Transport Package: Barrel Package in Pallet
Specification: 35*30
Origin: Dongying China
HS Code: 3208100000
Customization: Available
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Steel Structure Anti-Corrosion Epoxy Zinc Rich Primer Paint

1.Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxyresinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Highshielding property, superioranti-rustproperty, strongadhesion, and good oilandwaterresistance.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2.Surface treatment:
The steel surface is prepared to perfection, either by shot blasting or sand blasting to achieve an immaculate Sa2.5 level, or through meticulous manual rust-removal reaching St3 level.

3.Construction conditions:
Ensure optimal environmental conditions: the substrate temperature needs to be at least 3°C above the dew point with a relative humidity below 85% and wind force not exceeding level 3. Construction should be paused if substrate temperature falls below 5°C as the epoxy resin and curing agent will cease to react. Avoid unfavorable weather such as rain, fog, wind, sand, or condensation during mornings and evenings for outdoor projects.

4.Notes:
1. Begin by thoroughly stirring component A mechanically until uniform, then proceed to evenly blend with component B.
2. Continuously stir during the coating procedure to prevent sedimentation, as this can disrupt the balance between powder and liquid, potentially compromising the quality of the resulting paint film.
3. It is essential to achieve a dry film thickness of at least 70μm, with the application of 1 to 2 coats for optimal protection.
4. Once mixed, the two-component paint should ideally be used within 5 hours to maintain coating integrity. Prolonged use beyond this time frame may deteriorate the quality of the coating.
5. After usage, the curing agent must be securely sealed and utilized promptly to avert any degradation caused by reactions with atmospheric water vapor.