FD-H001 High Pressure Airless Spray Epoxy Zinc Coating - 20kg Matt Finish

Product Description

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxy resinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Highshielding property, superioranti-rustproperty, strongadhesion, and good oilandwaterresistance.

2.Surface treatment:
The steel surface is meticulously prepared with shot or sand blasting to achieve a pristine Sa2.5 level, or carefully manually cleaned to St3 level, ensuring optimal adherence.

3.Construction conditions:
Ensure that the substrate temperature remains 3°C above the dew point. Maintain relative humidity below 85% with wind force at or below level 3. If the substrate temperature drops below 5°C, the epoxy resin and curing agent cease to react, necessitating a halt in construction. Steer clear of construction during rainy, foggy, windy, and sandy conditions, as well as morning and evening condensation.

4.Notes:
1. Prior to use, employ mechanical stirring to achieve a uniform mix of component A, then seamlessly blend it with component B.
2. Consistently stir during application to prevent sedimentation, ensuring a balanced powder to liquid ratio and maintaining the integrity of the paint film.
3. Aim for a dry film thickness of ≥70μm through 1 to 2 coats for optimal protection.
4. Post-mixing, the two-component paint should be utilized within 5 hours to preserve quality. Exceeding this timeframe may compromise the coating's efficacy.
5. Upon depletion, the curing agent must be securely sealed and used promptly to avert losses due to reactions with ambient water vapor.