FD-H001 High Pressure Airless Spray Zinc Rich Epoxy Paint - Matt Finish

Product Description

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxyresinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Highshielding property, superioranti-rustproperty, strongadhesion, and good oilandwaterresistance.

2. Surface treatment:
The steel surface is shot blasted or sand blasted to Sa2.5 level, or manually rust-removed to St3 level.

3. Construction conditions:
The substrate temperature must be 3°C higher than the dew point, and relative humidity should be less than 85%. Wind force should be no greater than level 3. If the substrate temperature falls below 5°C, the epoxy resin and curing agent will cease to react, and construction must be halted. Avoid performing outdoor application on rainy, foggy, windy, and sandy days, as well as during morning and evening condensation.

4. Notes:
1. Prior to use, ensure component A is uniformly mixed using mechanical stirring, followed by thorough mixing with component B.
2. Consistently stir during the application process to avert sedimentation, which might disturb the powder to liquid ratio, thereby affecting the quality of the paint film.
3. It is advisable for the dry film thickness to be at least 70μm, with 1 to 2 coats completed.
4. Post-mixing, the two-component paint should ideally be consumed within 5 hours. Surpassing this timeframe may impair the coating quality.
5. After utilizing the curing agent, ensure the container is tightly sealed and utilize the remaining product promptly to prevent degradation due to reaction with moisture in the air.