FD-H001 Matt Epoxy Paint Primer for Air Spray and Brush

Name: FD-H001 Matt Epoxy Paint Primer for Air Spray and Brush
SKU: MIC-AtIROWBybeUG

FD-H001 two-component epoxy primer for steel substrates.

Reference price (FOB)

US $4-10 / kg

Quantity	Reference price
100-9,999 kg	USD 10.00 / kg
10,000-999,999 kg	USD 8.00 / kg
1,000,000+ kg	USD 4.00 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings Primers

Product specifications

Model NO.: FD-H001
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Transport Package: Barrel Package in Pallet
Specification: 35*30
Trademark: signal
Origin: Dongying China
HS Code: 3208100000
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Color: Grey
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Steel Structure Anti-Corrosion Epoxy Zinc Rich Primer Paint

1.Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxyresinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Highshielding property, superioranti-rustproperty, strongadhesion, and good oilandwaterresistance.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2.Surface treatment:
The steel surface is meticulously prepared by shot blasting or sand blasting to an impeccable Sa2.5 level, or manually polished with care to reach St3 level.

3.Construction conditions:
Ensure the substrate temperature maintains a steady 3°C above the dew point, with relative humidity comfortably below 85%, and wind force not exceeding level 3. Construction should be halted when temperatures fall below 5°C, as this prevents the reaction between epoxy resin and curing agent. Steer clear of rainy, foggy, or windy conditions, as well as sandy days and morning/evening condensation, especially during outdoor applications.

4.Notes:
1. Prior to application, employ mechanical stirring to achieve an even mixture of Component A, followed by the integration of Component B, ensuring consistency throughout.
2. Maintain periodic stirring during the coating process to prevent sedimentation, which could disrupt the crucial powder-to-liquid balance, thereby affecting the quality of the resultant paint film.
3. For optimal results, it's advised to maintain a dry film thickness of at least 70μm, applying 1 to 2 coats accordingly.
4. Once mixed, the two-component paint should ideally be utilized within a 5-hour window to uphold superior coating quality.
5. After the curing agent has been expended, ensure it is securely sealed and consumed promptly to mitigate potential reactions with atmospheric water vapor that could lead to unforeseen losses.