FD-H001 Matt Epoxy Primer Coating - Ideal for Indoor and Outdoor Use

Name: FD-H001 Matt Epoxy Primer Coating - Ideal for Indoor and Outdoor Use
SKU: MIC-WgtRHpvYuEkU

FD-H001 two-component epoxy primer for steel substrates. Intended for indoor and outdoor use. Supplied in liquid form.

Reference price (FOB)

US $4-10 / kg

Quantity	Reference price
100-9,999 kg	USD 10.00 / kg
10,000-999,999 kg	USD 8.00 / kg
1,000,000+ kg	USD 4.00 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings Primers

Product specifications

Model NO.: FD-H001
Color: Grey
Appearance: Liquid
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Trademark: signal
Transport Package: Barrel Package in Pallet
Specification: 35*30
Origin: Dongying China
HS Code: 3208100000
Customization: Available
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Hot Sales High-Performance Anti Rust Zinc Epoxy Primer for Steel Buildings

FD-H001 Matt Epoxy Primer Coating - Ideal for Indoor and Outdoor Use
1.Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxyresinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Highshielding property, superioranti-rustproperty, strongadhesion, and good oilandwaterresistance.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2.Surface treatment:
The steel surface is meticulously prepared, achieving Sa2.5 level through shot blasting or sand blasting, or manually reaching St3 level for rust removal.

3.Construction conditions:
For optimal results, ensure the substrate temperature exceeds the dew point by 3°C, with relative humidity below 85% and wind force no more than level 3. Construction should pause if the temperature drops below 5°C, as the epoxy resin and curing agent cease to react. Avoid construction during adverse weather conditions like rain, fog, wind, sand, and during morning or evening condensation for exterior work.

4.Notes:
1. Thoroughly mix component A using mechanical stirring, ensuring uniformity, before combining it with component B for a consistent application.
2. Stir regularly during application to prevent sedimentation that could disrupt the powder-liquid balance and compromise the paint film's quality.
3. Aim for a dry film thickness of at least 70μm, with one to two coats recommended for best coverage.
4. Use the two-component paint within 5 hours of mixing to maintain coating quality, as exceeding this timeframe may impact performance.
5. After using the curing agent, ensure it is tightly sealed and consumed promptly to prevent loss from reaction with atmospheric moisture.