FD-H001 Steel Building Anti-Rust Zinc Epoxy Primer

Name: FD-H001 Steel Building Anti-Rust Zinc Epoxy Primer
SKU: MIC-XAIRfFiJserp

FD-H001 two-component epoxy primer for steel substrates.

Reference price (FOB)

US $4-10 / kg

Quantity	Reference price
100-9,999 kg	USD 10.00 / kg
10,000-999,999 kg	USD 8.00 / kg
1,000,000+ kg	USD 4.00 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings Primers

Product specifications

Model NO.: FD-H001
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Transport Package: Barrel Package in Pallet
Specification: 35*30
Trademark: signal
Origin: Dongying China
HS Code: 3208100000
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Color: Grey
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Hot Sales High-Performance Anti Rust Zinc Epoxy Primer for Steel Buildings

FD-H001 Steel Building Anti-Rust Zinc Epoxy Primer
1.Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxy resinasthebasematerial, phosphorironpowder,rust-proofpigment,etc., and cured by polyamide.It ispacked by dual componentsAand B.Characteristics:Highshielding property, with superioranti-rustcapability, strongadhesion, alongside excellent oilandwaterresistance properties.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2.Surface treatment:
The steel surface should be shot blasted or sand blasted to a Sa2.5 level, or manually rust-removed to a St3 level.

3.Construction conditions:
The substrate temperature must remain 3°C above the dew point, with relative humidity below 85%, and wind force should not exceed level 3. If the substrate temperature dips below 5°C, the epoxy resin and curing agent will cease reacting, necessitating a halt in construction. Weather conditions such as rain, fog, high winds, or sandstorms, as well as morning and evening condensation, should be avoided for outdoor construction.

4.Notes:
1. Prior to usage, component A must be mixed thoroughly using mechanical stirring, followed by a uniform blend with component B.
2. Stirring should be done regularly throughout the coating process to prevent sedimentation, which can disturb the powder-to-liquid ratio and impact the overall quality of the paint film.
3. A recommended dry film thickness of ≥70μm should be achieved, with 1 to 2 coats applied for optimal results.
4. Once mixed, the two-component paint should ideally be used within 5 hours, as exceeding this timeframe might compromise the coating quality.
5. After the curing agent is used, ensure it is sealed tightly and consumed swiftly to avoid losses from reactions with air moisture.