FD-H001 Zinc Epoxy Primer for Sewage Plant Protection

Name: FD-H001 Zinc Epoxy Primer for Sewage Plant Protection
SKU: MIC-tApUPzHuueYo

FD-H001 two-component epoxy primer for steel substrates.

Reference price (FOB)

US $2.5-6.5 / kg

Quantity	Reference price
100-999 kg	USD 6.50 / kg
1,000-999,999 kg	USD 4.50 / kg
1,000,000+ kg	USD 2.50 / kg

Minimum order: 100 kg

Confirm the specification, quantity and shipping terms for your quotation.

Request a Quote

CategoriesAnti-Corrosion Coatings Primers

Product specifications

Model NO.: FD-H001
Main Raw Material: Epoxy
Method: Spray
Level: Primer
Drying Method: Air Drying
Substrate: Steel
Components: Film Forming Matter
Formation Mechanism: Conversion Type
Luster: Matt
Weight: 20kg/Barrel
Construction Method: High Pressure Airless Spray, Air Spray, Brush, Rol
Coating Thickness: Wet Film:80um Dry Film: 40um
After Sales Service: 5 Years
Transport Package: Barrel Package in Pallet
Specification: 35*30
Trademark: Singal
Origin: Dongying China
HS Code: 3208100000
Production Capacity: 50000ton/Year
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg
Lead Time: 7 days (1 - 1000 kg) To be negotiated ( > 1000 kg)
Number of components: Two-component
Color: Grey
Proportion: About 2.40
Dry Time: 23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio: 10:1
Coating thickness: Wet film:80um Dry film: 40um
Construction methord: High pressure airless spray, air spray, brush, roller
Shelf life: 12 months

Packaging & shipping

Transport Package: Barrel Package in Pallet
Specification: 35*30
Package Size: 30.00cm * 30.00cm * 35.00cm
Package Gross Weight: 20.000kg

Product description

Product Description

Product Name: Zinc Rich Epoxy Primer Sewage Plant Metal Protection Anti Corrosive Paint

1.Introduction:

Epoxyzinc_-richprimerisatwo_-componentcoatingwithepoxy resinasthebasematerial, enriched with phosphorironpowder,rust-proofpigment, and other high-performance ingredients, all expertlycured by polyamide.It isconveniently packed by dual componentsAand B, ensuring optimal performance.Characteristics:Boasting a highshielding property, this primer offers superioranti-rustprotection with strongadhesion. Its resilience extends to excellent oilandwaterresistance, promising long-lasting durability.

Number of components	Two-component
Color	Grey
Proportion	About 2.40
Dry Time	23±2°C Surface dry time ≤30min, Through dry time ≤24h, Fully cured 7 days
Mixing ratio	10:1
Coating thickness	Wet film:80um Dry film: 40um
Construction methord	High pressure airless spray, air spray, brush, roller
Shelf life	12 months

2.Surface treatment:
The steel surface should be meticulously shot blasted or sand blasted to Sa2.5 level, or manually rust-removed to St3 level, ensuring a pristine foundation.

3.Construction conditions:
For optimal conditions, ensure the substrate temperature is 3°C higher than the dew point, with relative humidity <85%, and wind force ≤ level 3. When temperatures drop below 5°C, the epoxy resin and curing agent cease to react, halting construction. Steer clear of rainy, foggy, windy, and sandy conditions, as well as morning and evening condensation for outdoor projects.

4.Notes:
1. Prior to application, employ mechanical stirring to achieve a uniform mix of component A before blending evenly with component B.
2. Regular stirring during the coating process is essential to prevent sedimentation and maintain an ideal powder to liquid ratio, safeguarding the quality of the paint film.
3. Aim for a dry film thickness of ≥70μm, completing 1 to 2 coats for best results.
4. After mixing, utilize the two-component paint within 5 hours to preserve coating quality.
5. Post-use, tightly cover the curing agent and use promptly to avert losses from reactions with moisture in the air.